Self-aligned quadruple patterning to meet requirements for fins with high density
Over recent decades, continuous reductions in the scale of field-effect transistors in accordance with Moore's law, which states that the number of transistors in an integrated circuit doubles every two years, have enabled continuous increases in device performance and transistor density.1–3 Currently, state-of-the-art devices are based on structural elements with dimensions of 7nm or even 5nm (N7/N5). The highest-resolution patterns required for N7/N5 devices are silicon fins with a pitch of 18–28nm and metal layers with a pitch of 24–32nm. These dimensions far exceed the resolution attainable with 193 immersion (193i) lithography. Extreme UV lithography might be an alternative process for the formation of lines and spaces, but is expensive and not entirely ready for use in production.4
We have developed a low-cost SAQP method that has the potential to meet these requirements for fins. We started with a 193i lithography pattern with a pitch of 90nm and lines and spaces of 40 and 50nm, respectively, which we transferred onto a mandrel. Then we deposited silicon dioxide (SiO2) spacers by atomic layer deposition (ALD) and etched them by a fluorine-based plasma. We removed the mandrel using an oxygen plasma. After cleaning the pattern with dilute hydrofluoric acid, we deposited a second set of SiO2 spacers by ALD and etched them by a fluorine-based plasma. This time, we removed the mandrel with a chlorine-based plasma. We transferred the quadruple pattern into a silicon nitride pad and bulk crystalline silicon. The plasma-enhanced ALD spacers were deposited by ASM. Figure 1 shows a simulation of the patterning process produced using Coventor software.
In this SAQP method, each patterning step gives a CDU value in the sub-nanometer range (3 sigma). As well as controlling the CDU, we developed plasma etching processes that generate vertical profiles, paying special attention to the mandrels. Figure 2 shows transmission electron microscopy (TEM) cross-sectional images of each SAQP step until the nitride pad etching step. After we completed the fin patterning, our preliminary results were as follows: a fin top CD of 7nm (measured by TEM); a fin CDU of 0.6nm (3 sigma); an average pitch walk of 0.5nm with a 3 sigma of 0.8nm; and a fin height of 115nm with a straighter profile on the top 50nm (see Figure 3).
In contrast to the sub-nanometer fin CDU and pitch walk, the exacting specifications for LER and LWR were more challenging to attain. After lithography, we carried out a roughness analysis of 131 images across a wafer of 300mm. The average values of LWR and LER were 4.2 and 2.9nm, respectively, which confirms that the line edges were uncorrelated (see Figure 4, left). After SAQP, a roughness analysis revealed that the LWR was about 1.2nm and the LER about 2.2nm, which suggests that the line edges were correlated. After etching of fins, analysis of power spectral density (PSD) showed that the LER was lower than the LWR at high frequency (10−1 to 10−1.7nm−1). However, the major contribution to the high LER is found at middle and low frequencies (10−1.7 to 10−3.5nm−1), which suggests that the lines became wavy at low frequencies.
Note that one of the most important factors in achieving high performance in SAQP is the reliance on measurement techniques, which need to have sufficient resolution to determine the roughness of small features. We have optimized the settings of CD scanning electron microscopy, such as averaging, field of view, and pixel size, for the determination of LER and LWR.7 We have also demonstrated the interpretation and feed-forward of data from scatterometry to improve the control of pitch walk.8
The performance of SAQP that we have achieved is quite close to the specifications of the technology. However, the control of certain parameters needs to be improved, such as the control of LWR and LER at the photoresist level and during the etching steps. We have identified key methods that promise to enable improvements in LER (soft-plasma treatment of the photoresist), pitch walk (optimizing plasma-enhanced ALD), and CDU and profile (optimizing the etching process). Simulations using Coventor software will be used to test our assumptions in order to attain the target specifications.
National Center of Scientific Research ‘Demokritos’